In this study the effect of basicity of catalyst is investigated using different metal oxide supported Nickel and Ruthenium catalyst. The basic strength of catalysts was orchestrated with using different types of metals and different composition of supports. In this study Al2O3-CaO, Al2O3-MgO, Al2O3-BaO supports were used with nickel and ruthenium catalyst, which synthesized with sol-gel method. Different mass ratios of supports were used such as; 100%, 70%/30%, %50/50%, 20%/80% respectively. For all metal oxides Nickel loadings are 1 %, 5% and Ruthenium loading is 0.5%. Calcination temperature was 500 0C with 6 hours. All catalysts were used in methanation reaction with conditions varies between 300-600 0C, inlet ratio of CO2/H2 1/4 to 1/6 and GSHV 5000h-1/10000h-1. The products were analyzed using GC and catalysts were analyzed using XRD NH3-TPD and BET. Nickel load selected as 1%, magnesium supported catalysts' the main crystallites were aluminum oxide and magnesium oxide for 30%,50%,80; respectively. Calcium supported catalyst had had alumina and calcium oxide crystallites for 30%,50% respectively. Barium supported catalysts had had alumina and barium mix oxide crystallites for 30%,50% respectively. For 5% Nickel loaded 70-30% alumina magnesia mix oxide catalyst magnesia and alumina crystallites are found. Aluminum magnesium mix oxide catalysts had higher basicity than aluminum barium mix oxide catalysts for 1% nickel catalysts. Ruthenium based magnesium alumina mix oxide catalyst had higher basicity than nickel-based magnesium alumina catalysts. Ruthenium catalysts had higher total performance towards both of the reverse water gas shift reaction and carbon dioxide methanation than nickel-based catalysts.