Market share of the can coating industry was 2 billion dollars in 2018 globally. A large portion of this market is focused on protecting valuable goods such as foods and cosmetics. Recent bans on the Bisphenol A(BPA) created a BPA-free coating demand due to the high portion of BPA based coatings in the industry such as epoxy. A conventional epoxy based (EP) can coating was compared with a new design of BPAfree polyester coating(PE). Atomic Force Microscopy(AFM), Scanning Electron Microscopy(SEM), Electron Dispersive Spectroscopy(EDX), Electrochemical Impedance Spectroscopy(EIS), Direct Current(DC) Polarization were used to investigate degradation. Industrial and model tinplate samples are compared with surface investigation methods. AFM results indicate the surface composition difference. To investigate bare tinplate corrosion, a mixture of acidic electrolyte was prepared and compared with other conventional aging electrolytes, containing mono acids. The electrolyte prepared from mixed acids was found to have the highest detinning abilities. Therefore, coated samples were aged with this mixed acid solution electrolyte. EIS results indicated that the type of electrolyte alters the corrosion mechanism, indicated by the observance of different time constants at different time scales. During immersion tests, EP based coatings showed better corrosion resistance as shown by higher impedance at low frequency, higher coating resistance and lower capacitance values. However, after sterilization, polyester coated samples showed better corrosion protective abilities (indicated by lower amount of corrosion products and higher impedance values) compared to the epoxy sample even though AFM measurements indicated that it had larger pore sizes after aging compared to epoxy sample. These results are attributed to the larger electrochemical area and higher diffusion properties of EP coatings, obtained after modelling of EIS data.