Preparation and characterization of chitosan/calcium phosphate based composite biomaterials/Oktay Yıldırım; thesis advisor Muhsin Çiftçioğlu.
tarafından
Yıldırım, Oktay.
Başlık
:
Preparation and characterization of chitosan/calcium phosphate based composite biomaterials/Oktay Yıldırım; thesis advisor Muhsin Çiftçioğlu.
Yazar
:
Yıldırım, Oktay.
Yazar Ek Girişi
:
Yıldırım, Oktay.
Yayın Bilgileri
:
[s.l.]: [s.n.], 2004.
Fiziksel Tanımlama
:
xvi, 97 leaves.: ill.+ 1 computer laser optical disc.
Özet
:
In this study the preparation and characterization of three-dimensional chitosan-calcium phosphate composite structures and porous hydroxyapatite bodies for biomaterial applications have been studied. The effects of chitosan calcium phosphate amount on density, porosity, microstructure, chemical composition and mechanical properties on the composites and effects of porosifier contents, hydroxyapatite content of the slurry and sintering temperature on density, porosity and microstructure of the porous ceramic samples were investigated. SEM was used for microstructural analysis, XRD and FTIR were used for chemical analysis, Archimedes method was used for investigating physical properties and compression test for investigating mechanical properties. In this study low molecular weight chitosan, -tricalciumphosphate, hydroxyapatite and hydroxyapatite whisker have been used. For composites freeze drying technique and for the porous bodies dry pressing, polymer sponge method and dough method have been used.The densities of the composites prepared by using chitosan as the matrix and hydroxyapatite, hydroxyapatite whisker, and B-tricalciumphosphate as reinforcement increased and the porosities decreased with the increase in the ceramic content. The modulus of elasticity and the yield stress generally increased with the increasing ceramic content except for the chitosan/-tricalciumphosphate composites. The densities and porosities of the composite structures varied in the range of 0.059-0.29 g/cm3 and 96-88% respectively. The elastic moduli of the composites varied in a range of 4.45-10.09 MPa and yield stress varied in a range of 0.14-0.34 Mpa due to the change in the ceramic weight%. Changing the ceramic weight% also had influence on the microstructure. Generally with increasing ceramic content the pore sizes decreased.The pore sizes varied in a range between 100-250, 100-400 and 100-200 for chitosan/hydroxapatite, Chitosan/-TCP/Hydroxyapatite and chitosan/HA whisker composites respectively. FTIR and XRD analysis showed that the composite structures contained original constituents, no new chemical compounds were formed the production process had not affected crystallinity of ceramic phases. The densities of the porous ceramic bodies decreased and the porosities increased with the increasing porosifier content at the porous ceramics prepared by dough method and dry pressing method. The porosity and density values of porous hydroxyapatite samples changed in range of 34-72% and 2.03 to 0.87 g/cm3. Pore sizes of polymeric sponge samples were found to be around 300-400 and dry pressing and dough method samples were found to be 10u.
Konu Başlığı
:
Chitin -- Biotechnology.
Biomedical materials
Chitosan
Calcium phosphate
Yazar Ek Girişi
:
Çiftçioğlu, Muhsin
Tüzel Kişi Ek Girişi
:
İzmir Institute of Technology. MaterialsScience and Engineering.
Tek Biçim Eser Adı
:
Thesis (Master)--İzmir Institute of Technology:Materials Science and Engineering
İzmir Institute of Technology:Materials Science and Engineering--Thesis (Master).
Elektronik Erişim
:
Library | Materyal Türü | Demirbaş Numarası | Yer Numarası | Durumu/İade Tarihi |
---|
IYTE Library | Tez | T000452 | TP248.65.C55.Y52 2004 | Tez Koleksiyonu |