Development of colloidal alloyed nanocrystals for quantum dot based device applications için kapak resmi
Development of colloidal alloyed nanocrystals for quantum dot based device applications
Başlık:
Development of colloidal alloyed nanocrystals for quantum dot based device applications
Yazar:
Sevim Ünlürürk, Seçil, author.
Fiziksel Tanımlama:
xxiv, 159 leaves: illustrarions, charts;+ 1 computer laser optical disc.
Özet:
Quantum dots (QDs) are very attractive luminescent semiconducting nanoparticles. In this study, our aim was to synthesize Cd and/or Zn based QDs with tunable optical properties by the particle size and the alloy composition. Colloidal water dispersible Mn-doped and nondoped ZnSxSe1-x QDs were synthesized by the one-pot aqueous method. Optical measurements indicate that photoluminescent properties are strongly depended on the capping agent. While MPA capped QDs showed an emission peak in the blue region, others did not show any photoluminescence at all. Mn doping up to 10% resulted in no significant effect on the optical spectra. However structural characterizations, EPR and XRD, supported that Mn ions were bounded to the 220 and 311 facets of QD. ZnxCd1-xSySe1-y quaternary nanoalloys were synthesized by using a modified two-phase approach for the first time in the literature. Optical properties of highly luminescent ZnxCd1-xSySe1-y nanoalloys were tuned from blue to yellow by the particle size, the alloy composition, and thickness of shell layer. The reactivity of the reactants, initial mole ratios, and other reaction parameters was adjusted to control alloy composition and alloy type: homogeneous and gradient. The reaction time controls the size of particles. The PL QE (up to 52%) and lifetimes (about 25 ns) were found similar regardless of core and core-shell nanoalloys. MicroPL measurements were carried out on ZnxCd1-xSySe1-y nanoalloys by fiber spectrometer integrated to confocal microscope. Photobleaching and blue-shifting, about 6 nm, were observed in the microPL spectra. Photobleaching times and rate constants obtained from single exponential decay curves showed that purification and exposure time are strongly effective. Additionally, the power the excitation light is essential that below 11 μW, photobleaching slows down, and at 2 μW there is no photobleaching. Scale-up methods with high-volume batch and flow reactor were used to synthesize CdTe and ZnxCd1-xSySe1-y QDs. LEFETs were fabricated with TUBITAK support in collaboration with Heidelberg University. PbS QDs were used as emitting material at the bottom contact top-gate unipolar LEFETs in which uniform electroluminescence was obtained.
Yazar Ek Girişi:
Tek Biçim Eser Adı:
Thesis (Doctoral)--İzmir Institute of Technology:Chemistry.

İzmir Institute of Technology:Chemistry--Thesis (Doctoral).